1、 无机富锌底漆 1500ASD Zinc 1500A 无机富锌底漆 1500APRODUCT DESCRIPTION A solvent tupe self-curing inorganic zinc rich costing based on alkylsilicate binder& INTENDED USES产品简介 烷基硅酸脂为原料的溶剂型自干型无机富锌涂料FEATURES 产品特性 Remarksble corrosion resistance极佳的防腐性能 Outsanding resistance to impact,mechanical abrasion and organic
2、 solvent 优良的耐冲击，耐磨损和耐有机溶剂性能High-build applicability极好的厚涂施工性能Remakable heat resistance and less scorch by heat treatment优良的耐热性，热处理烧损少Good applicability by standard airless spray equipment.适用于标准无空气喷涂设备。 Coefficient of friction is higher.能够提供较高的摩擦系数。BASIC DATA基本数据Color(s) Grey颜色 灰色Mising tatio Liquid/P
3、owder=23/77(by wt)混合比率 液体/粉末=23/77（重量比）Solid content 87%重量固体份 Film thickness Dry:75microns/cost Wet:125 microns/cost涂装膜厚 干膜：75um/道 湿膜：125 um/道Spreading tate Theoretical:0.350/kg/75microns涂覆率 理论值：0.350 千克/平方米/75umPractical:Varies depending on surface conditions, environment,application,etc.实际值：与表面处理，
4、外界环境，施工方法等多种因素有关。STORAGE存储Flash point Greater than20闪点 20以上Shelf life 6months储存期限 6 个月Shelf tempterature -10-40储存温度 APPLICATION DATA施工数据Pot life混合使用期 Temperature()温度 5 10 20 30Pot life(hrs) 混合使用期8 7 6 5Application methods施工方法Airless spray,air spray,brush and roller无气涂料，空气涂料，刷涂及琨涂Airless spray 无气涂料 R
5、ecommended 推荐Nozzle tip 喷嘴尺寸 0.021-0.023Fluid pressure 出口压力 75-125kg/cThinning 稀释比例 0-5% by volume(体积比)Thinner SD Zinc 1500 Thinner稀释剂 专用稀释剂Application temperature 5-40施工温度Drying time &Overcosting interval干燥时间及涂装间隔Temperature() 温度 5 10 20 30Dry to touch(mins)指触干燥 60 60 30 20Dry hard(hrs) 半硬干燥 6 4 3
6、2Min.interval(hrs) 最小涂装时间48 48 48 48Max.interval(days) 最大图装时间- - - -PAINTING SYSTEM涂装配套Applied substrates Bare steel.etc.适用底材 裸钢等Subsequent cost Epomarine EX500,EpomarineEX600, pomarine SuperEX 21,or according to the costing systems of Kansai.适用上涂 Epomarine EX500,EpomarineEX600, pomarine SuperEX 21,
7、或参考我公司推荐配套。SURFACE PREPARATION表面处理 Remove salt and other water-soluble contaminants by fresh water hosing用清水冲去盐分及其他水溶性污物。 Degrease according to SSPC-SP1 solvent cleaning.依照 SSPC-SP1 溶剂清洗标准除去油脂。 Remove weld spatter and smooth weld seams and sharp sdges.除去焊接飞溅并处理焊缝，毛刺使用其光顺。 Remove rust,mill-scale and
8、damaged shop primer by blasting to ISO Sa2.5(SSPC-SP10) or by power tooling to ISO St3.用喷砂方式除去铁锈，氧化皮和损坏的车间底漆达到 ISO Sa2.5(SSPC-SP10)或用动力工具处理表面达到 ISO St3. Remove dust and dirt by highpressure air before paint application.用高压空气吹扫除去灰尘等污物。 Be sure that the surface is clean and dry prior to application。施工前请确认表面清洁干燥。