1、1磁化率的测定数据处理一、原始数据记录室温： 压强：磁外空管平均值磁内空管平均值磁外样品平均值磁内样品平均值 m 空管 m 样品 m 样品-m 空管 m/g莫尔氏盐 18.3210 18.3189 25.7924 25.9545h=11.2cm 18.321118.3210518.318918.3189025.792525.7924525.954625.95455 -0.00215 0.16210 0.16425 7.47140硫酸亚铁 19.8665 19.8645 25.9549 26.1546h=10.6cm 19.866519.8665019.864519.8665025.954925
2、.9549026.154626.15460 -0.00200 0.19970 0.20170 6.08840铁氰化钾 17.7280 17.7252 24.3152 24.3493h=10.9cm 17.728017.7280017.725217.7252024.315124.3151524.349324.34930 -0.00280 0.03415 0.03695 6.58715亚铁氰化钾18.8117 18.8089 25.1800 25.1725h=11.1cm 18.8117 18.8117018.8089 18.8089025.180126.1800525.175226.17520
3、-0.00280 -0.00485 -0.00205 7.368352二、计算莫尔氏盐磁化率，求出磁感应强度；再由标准样品求出其余样品磁化率1、计算莫尔氏盐磁化率 T=26.5=299.65K M 莫氏盐 =392.14=3.970710-7 m3/kg=1.557110-7m3/mol4.93810T相应的磁场强度H= = =2.9386 T02()AMmgh20.164259.8392.14410-77.471401.557110-7 7102、由标准样品求出其余样品磁化率相关数据如下：样品 A（ ）/g空莫 氏 盐 mH/cm m/g莫尔氏盐 392.14 0.16425 11.2 7.
4、47140硫酸亚铁 278.03 0.19970 10.6 6.08840铁氰化钾 329.25 0.03415 10.9 6.58715亚铁氰化钾 422.39 -0.00485 11.1 7.36835样品摩尔磁化率可由以下公式求的： 校 准 剂校 准 剂样 品校 准 剂样 品样 品校 准 剂空校 准 剂 空品样样 品 hMmm)(则有： 莫 氏 盐莫 氏 盐硫 酸 亚 铁莫 氏 盐硫 酸 亚 铁硫 酸 亚 铁莫 氏 盐空莫 氏 盐 空硫 酸 亚 铁硫 酸 亚 铁 )(=0.199700.164257.471406.08840278.03392.1410.611.21.557110-73/
5、=1.558910-73/同理有：铁氰 化 钾 =0.034150.164257.471406.58715329.25392.1410.911.21.557110-73/3=0.300110-73/亚铁氰 化 钾 =-0.004850.164257.471407.36835422.39392.1411.111.21.557110-73=0.0497710-73/3、根据 m计算样品的未成对电子数a、硫酸亚铁由 得：72104KTNA= 3410-7=31.558910-71.3806621023299.656.021023410-7 2/25.057310232/2b、铁氰化钾= 3410-7
6、=30.300110-71.3806621023299.656.021023410-7 2/22.218910232/2又因为 、 B=9.27407810-24，所以：当 n=1 时， m=1.606310-23 J2/T2；当 n=2 时， m=2.623110-23 J2/T2；当 n=3 时， m=3.591810-23 J2/T2；当 n=4 时， m=4.543410-23 J2/T2；当 n=5 时， m=5.486610-23 J2/T2。由此可以看出:当 n=4 时， m=4.543410-23 J2/T2，接近，则硫酸亚铁的未成对电子数是 4。=5.057310232/2当 n=2 时， m=2.623110-23 J2/T2，接近，则铁氰化钾的未成对电子数是 2。=4.543410232/2因为 ，故亚铁氰化钾是反磁性物质，未成对亚铁氰 化 钾 =0.0497710-73/电子数为 0。45